In recent years, the coating is basically a pre-coated film. Due to the short time of use and the many problems that occur, according to process practice, the main factors affecting the quality of the pre-coating film are temperature and pressure. The three factors of speed, so correctly handling the relationship between the three is critical to ensure the quality of the pre-coating film and the impact on the production of the next process.
Paper-plastic coating will be the comprehensive result of the physical function of hot pressing. Temperature, pressure and speed are the three basic factors to achieve this physical comprehensive effect. Correctly handling the relationship between these three is the key to the process operation technology.
Temperature: It is the first key to coating. The adhesive used for pre-coating is hot melt adhesive. Temperature determines the melting state of hot melt adhesive, determines the leveling performance of hot melt adhesive, and determines the molecular orientation of hot melt adhesive. The diffusion ability of three substances, such as BOPP film, printing ink layer, paper substrate, etc., also determines the crystallinity of the hot melt adhesive. Only by correctly controlling the temperature of the working area can the solid heat of the pre-coated film on the film be made The melted adhesive layer melts completely into a viscous flow state, with suitable fluidity to achieve wetting and bonding to the surface of the printed matter, while ensuring immediate solidification after compounding. Make the laminating product flat, bright enough, the adhesive layer melts well, without creases. And can peel off the ink. The temperature control of the coating process also affects and determines the hot-melt adhesive used for the coating to solve the changes when heated, and the resistance to the new heat. Therefore, strict temperature control is the primary key to pre-coating. According to our practice. Temperature control in the range of about 80 ~ 100C is more appropriate.
Pressure: Appropriate pressure should be used while correctly controlling the lamination temperature, because the surface of the paper itself is not very smooth, only under the pressure, the hot melt adhesive in the state of viscous flow will drive away the air on the surface of the printed matter. Fully wet the paper print surface. Produce colloid molecules to the ink layer of paper printed matter, paper molecules, dislocation, and achieve good adhesion, forming a complete coverage of the entire surface of the printed matter, so that the printed matter is bright, no fog, leveling of the glue layer, no creases , The bonding effect is good. Under the condition of no wrinkle, the pressure should be increased properly to make the thermoplastic curing function of the hot melt adhesive fully displayed. In order to ensure that the laminating products are added after compounding. It has strong resistance to various physical peeling and impact forces. (Such as indentation, hot stamping, hot melt adhesives, etc.) to achieve the perfect uniformity of the internal structure and surface state of the composite printed matter.
Speed: Paper-covering is a dynamic compound motion. The movement speed determines the time that the paper-plastic composite stays on the hot-pressed working interface of the hot-pressed body, and also determines the temperature and pressure input by the laminating machine and the paper-plastic complex cooperation in the actual production process. Actual value. When the film temperature and pressure are fixed. The change in speed will change the effect of the coating, and due to the upper temperature limit and the pressure supply limit, it will only change from the direction less than the set value, and with the speed increase, the decrease will be obvious, and the hot pressure force will decline. Make the composite effect worse. Running speed is too fast. The bond is not strong. There will be fog, but too slow to be inefficient. Even bubbles. So the compound running speed. Decided the time for the pre-coated film and paper print to achieve bonding. According to our experience, the general speed control is more suitable for about 10-20 sheets of paper in one minute. (The speed of the electronic laminating machine is smaller due to the hot pressing roller. The speed should be slower)
The actual action value of the three factors of temperature, pressure and speed has a certain range. Due to different equipment. This requires us to find the best effect value in practice to ensure the composite effect of the pre-coating film and create favorable conditions for the spine of the cover of the next step of the adhesive nail cover not to leave the shell and not foam. The compounding of the pre-coating film and how to create favorable conditions for the following processes (including indentation, bronzing, and wireless binding on the cover, etc.) are also one of the important factors that we should consider in the process of using the pre-coating film for the laminating operation. When the pre-coated film is combined with the paper print. The lower limit is 80C and the upper limit is 100C. Intuitively based on the high brightness, no fogging, good flatness and no blistering after the composite body is detached from the hot-pressing roller, in this temperature range, the hot melt adhesive can fully receive the heat from the outside to the deep inside Function, the modification of various raw materials in the colloid can be fully exerted, and the entire adhesive layer is completely melted. It produces a true and firm bond, rather than a superficial, shallow layer, which can not be bent or reheated.
When the lower limit temperature is slightly downward, the brightness of the composite product will decrease. When the upper limit temperature rises slightly, bubbles that are not smooth and have different shapes will be scalded on the surface of the film. (This phenomenon is particularly obvious in the electronic laminating machine) Just grasp the critical working area of ​​the laminating temperature. Not only the composite effect is good, but also the hot melt colloid is close to the hot spot of the cross-linking reaction. The curing of the colloid is almost hard, so that it will not be easily softened when it is heated again. This film temperature is very close to the cross-linking reaction temperature.
Plastic card album is a peripheral product specially designed for card games to prevent the card from being damaged during play.
Plastic Card album
9 Pocket Binder Card Book,Rigidity And Tough Card Book,Board Games Card Box ,Trade Card Deck Box
Zhiling technology development (guangdong) co. LTD , https://www.sentebox.com